[Technology] Heat treatment process for casting magnesium alloy castings

The purpose of heat treatment of magnesium alloy castings is to improve its mechanical properties, such as tensile strength, yield strength, elongation or plasticity, hardness and impact toughness, to varying degrees. Some heat treatment is to reduce the casting casting stress or quenching stress and the growth tendency when working at high temperature, so as to achieve the purpose of stable size.

Whether the magnesium alloy can be strengthened by the heat treatment, that is, its mechanical properties, depends on whether the solubility of each component in the solid solution in the alloy changes with the temperature. Diffusion of magnesium is slow in the process of diffusion and decomposition of solid solution. Therefore, the heating time is longer in solid solution and aging treatment, and the solid solution does not decompose when cooled in air or hot water.

Magnesium alloys are not sensitive to natural aging and can remain in the quenched state at room temperature after quenching. Some alloys require artificial aging in order to increase the yield strength, and the holding time during artificial aging is also longer.

Magnesium alloys tend to oxidize more strongly than aluminum alloys, so the heating temperature of magnesium alloys should be accurately controlled. To prevent oxidation, the protective gas must be introduced into the furnace as often as so: or a certain amount of pyrite ore JA is placed in the furnace. To prevent oxidation or combustion of magnesium alloys.

China Ribbed Reinforcing Bar, Round Reinforcing Bar supplie,TMT bar 10mm-32mm TMT bar/ steel reinforcing bars for construction,Reinforcing steel bar, rebar, deformed steel bar, TMT bar

Reinforcing steel bars, rebar, Deformed steel bars
Size: 8mm-32mm Steel Grade:

HRB335, HRB400, HRB500, A615 Gr40, Gr60,BS4449 G460B, G500B

JIS SD390, SD490, KS SD40,  SD50

Length:  6m-12m  MOQ each size: 200MT.
Loading port:  Tianjin or any other port china. Packing: in bundle. 

 

Payment term 

LC  , TT  Application:  Building, bridge , road or project construction

Technical Parameter of HRB400:

HRB400

Chemical

Composition(%)

C Mn Si P S
0.25max  1.60max  0.80max 0.045max  0.045max 

Mechanical

Property

Yield Strength    Tensile Strenth   Elongation
 400Mpa min 540Mpa min  16%

Technical Parameter of HRB 500:

HRB500

Chemical

Composition(%)

 

 C   Mn  Si  P   S
 0.25max  1.60max  0.80max  0.045max  0.045max
 

Mechanical

Property 

 Yield Strength   Tensile  Strength   Elongation
 500Mpa min    630Mpa min  15%

Technical Parameter of HRB 335: 

HRB335

  Chemical

Composition (%)

 C  Mn  Si  P   S
 0.25max  1.60max  0.80max  0.045max  0.040max

    Mechanical

     Property

 Yield Strength    Tensile strength  Elongation
  335Mpa min   455Mpa min  17%
reinforcing bar

Reinforcing Bar

Reinforcing Bar, Ribbed Reinforcing Bar, Round Reinforcing Bar, Iron Reinforcing Bar

Hebei Dongshengyuan Trading Co.,Ltd. , http://www.wiremeshdsy.com